Colored glass plate and method for its production

ABSTRACT

To provide a colored glass plate which, despite the content of expensive cerium controlled to be low, simultaneously satisfies low solar transmittance, high visible light transmittance and low UV transmittance, while transmitted light has a green color tone. The colored glass plate comprises, as represented by mass percentage based on oxides, SiO 2 : from 65 to 75%, Al 2 O 3 : from 0 to 6%, MgO: from 0 to 6%, CaO: from 5 to 15%, total iron calculated as Fe 2 O 3 : from 0.3 to 1.2%, total titanium calculated as TiO 2 : from 0.2 to 1.1%, total vanadium calculated as V 2 O 5 : from 0.02 to 0.3%, and total cerium calculated as CeO 2 : from 0.01 to 0.5%, and contains substantially no cobalt, chromium or manganese.

TECHNICAL FIELD

The present invention relates to a colored glass plate which simultaneously satisfies low solar transmittance, high visible light transmittance and low UV transmittance, while transmitted light has a green color tone, and a method for its production.

BACKGROUND ART

As a glass plate for automobiles, a colored glass plate (e.g. a heat-absorbing glass plate or a UV-absorbing glass plate) is known, which contains a colorant component whereby transmitted light has a green or blue color tone.

For such a colored glass plate, the solar transmittance is required to be low (e.g. the value, as calculated in a thickness of 4 mm, of solar transmittance (hereinafter referred to also as Te) stipulated in JIS R3106 (1998) is required to be at most 55%). Further, the visible light transmittance is required to be high (e.g. the value, as calculated in a thickness of 4 mm, of visible light transmittance (illuminant A, 2 degrees field of vision) (hereinafter referred to also as Tv) stipulated in JIS R3106 (1998) is required to be at least 70%). Further, the UV-transmittance is required to be low (e.g. the value, as calculated in a thickness of 4 mm, of UV-transmittance (hereinafter referred to also as Tuv) stipulated in ISO-9050 is required to be at most 12%).

Further, as such a colored glass plate, a glass plate tends to be preferred such that when a passenger watches the scenery through the glass plate, the color tone of the transmitted light has a green color tone being a more natural color tone (e.g. the dominant wavelength (hereinafter referred to as also as Dw) of transmitted light stipulated in JIS Z8701 (1982) is from 540 to 570 nm).

Further, for such a colored glass plate, it is desired that types of colorant components be reduced as far as possible and that unit prices of raw materials for colorant components be low, from the viewpoint of costs and with a view to preventing inclusion of impurities at the time of changing the base material (i.e. changing the product type) in the melting furnace to be used for the production of glass.

As colored glass plates whereby transmitted light has a green color tone, for example, the following (1) to (3) have been proposed.

(1) Green glass comprising, per 100 parts by mass of a soda lime silica glass matrix composition,

-   -   total iron calculated as Fe₂O₃: from 0.5 to 2.0 parts by mass,     -   total titanium calculated as TiO₂: more than 1.0 part by mass         and at most 3.0 parts by mass,     -   CoO: from 0.003 to 0.02 part by mass,     -   Se: from 0 to 0.0008 part by mass,     -   total chromium calculated as Cr₂O₃: from 0 to 0.05 part by mass,     -   total vanadium calculated as V₂O₅: from 0 to 0.5 part by mass,         and     -   total cerium calculated as CeO₂: from 0 to 0.5 part by mass,         wherein the mass proportion of bivalent iron calculated as Fe₂O₃         in the total iron calculated as Fe₂O₃ is from 31 to 50%.

(2) UV-absorbing green glass made substantially of soda lime silica glass and comprising, as represented by mass percentage based on oxides,

-   -   total iron calculated as Fe₂O₃: from 0.45 to 0.491%,     -   total cerium calculated as CeO₂: from 1.09 to 1.2%,     -   total titanium calculated as TiO₂: from 0.3 to 0.39%, and     -   CoO: from 0 to 0.0003%,         wherein the mass proportion of bivalent iron calculated as Fe₂O₃         in the total iron calculated as Fe₂O₃ is from 30.5 to 32.0%.

(3) UV-absorbing green glass made substantially of soda lime silica glass and comprising, as represented by mass percentage based on oxides,

-   -   total iron calculated as Fe₂O₃: from 0.52 to 0.63%,     -   total cerium calculated as CeO₂: from 0.9 to 2%,     -   total titanium calculated as TiO₂: from 0.2 to 0.6%, and     -   CoO: from 0 to 0.002%,         wherein the mass proportion of bivalent iron calculated as Fe₂O₃         in the total iron calculated as Fe₂O₃ is from 31 to 38%.

However, the green glass of (1) has a problem such that since the content of CoO is large, Tv is low, and Dw is also low (i.e. transmitted light is bluish green). On the other hand, in the case of the UV-absorbing green glasses of (2) and (3), the content of CoO is small, and the content of total cerium calculated as CeO₂ is large, whereby Tv is high, and Tuv is sufficiently low.

However, recently, the prices for cerium raw materials have gone up, and accordingly the cost for green glass having a large content of total cerium calculated as CeO₂ has gone up. Therefore, a colored glass plate is desired which, despite the content of cerium controlled to be low, simultaneously satisfies low solar transmittance, high visible light transmittance and low UV transmittance, while transmitted light has a green color tone.

PRIOR ART DOCUMENTS Patent Documents

Patent Document 1: Japanese Patent No. 3,256,243

Patent Document 2: Japanese Patent No. 3,900,550

Patent Document 3: Japanese Patent No. 3,190,965

DISCLOSURE OF INVENTION Technical Problem

The present invention is to provide a colored glass plate which, despite the content of expensive cerium controlled to be low, simultaneously satisfies low solar transmittance, high visible light transmittance and low UV transmittance, while transmitted light has a green color tone.

Solution to Problem

The colored glass plate of the present invention is characterized by comprising, as represented by mass percentage based on oxides,

-   -   SiO₂: from 65 to 75%,     -   Al₂O₃: from 0 to 6%,     -   MgO: from 0 to 6%,     -   CaO: from 5 to 15%,     -   total iron calculated as Fe₂O₃: from 0.3 to 1.2%,     -   total titanium calculated as TiO₂: from 0.2 to 1.1%,     -   total vanadium calculated as V₂O₅: from 0.02 to 0.3%, and     -   total cerium calculated as CeO₂: from 0.01 to 0.5%,         and containing substantially no cobalt, chromium or manganese.

The colored glass plate of the present invention preferably further contains, as represented by mass percentage based on oxide, from 5 to 18% of Na₂O.

The colored glass plate of the present invention preferably has

-   -   a solar transmittance (Te) as stipulated in JIS R3106 (1998) of         at most 55% as a value calculated in a thickness of 4 mm,     -   a visible light transmittance (Tv) (illuminant A, 2 degrees         field of vision) as stipulated in JIS R3106 (1998) of at least         70% as a value calculated in a thickness of 4 mm,     -   an UV transmittance (Tuv) as stipulated in ISO-9050 of at most         12% as a value calculated in a thickness of 4 mm, and     -   a dominant wavelength (Dw) of transmitted light as stipulated in         JIS Z8701 (1982) of from 540 to 570 nm.

The method for producing a colored glass plate of the present invention, comprises melting glass raw materials, followed by forming to obtain a colored glass plate comprising, as compositional components of the glass plate after the forming and as represented by mass percentage based on oxides,

-   -   SiO₂: from 65 to 75%,     -   Al₂O₃: from 0 to 6%,     -   MgO: from 0 to 6%,     -   CaO: from 5 to 15%,     -   total iron calculated as Fe₂O₃: from 0.3 to 1.2%,     -   total titanium calculated as TiO₂: from 0.2 to 1.1%,     -   total vanadium calculated as V₂O₅: from 0.02 to 0.3%, and     -   total cerium calculated as CeO₂: from 0.01 to 0.5%,         and containing substantially no cobalt, chromium or manganese.

In the method for producing a colored glass plate of the present invention, it is preferred that the glass plate further contains, as its compositional component and as represented by mass percentage based on oxide, from 5 to 18% of Na₂O.

In the method for producing a colored glass plate of the present invention, it is preferred to obtain the colored glass plate which has

a solar transmittance (Te) as stipulated in JIS R3106 (1998) of at most 55% as a value calculated in a thickness of 4 mm,

a visible light transmittance (Tv) (illuminant A, 2 degrees field of vision) as stipulated in JIS R3106 (1998) of at least 70% as a value calculated in a thickness of 4 mm,

an UV transmittance (Tuv) as stipulated in ISO-9050 of at most 12% as a value calculated in a thickness of 4 mm, and

a dominant wavelength (Dw) of transmitted light as stipulated in JIS Z8701 (1982) of from 540 to 570 nm.

The above expression “to” to represent a numerical range, is used to include the numerical values given before and after the expression as the lower limit value and the upper limit value, respectively, and hereinafter in this specification, the same expression “to” is used to have the same meaning, unless otherwise specified.

Advantageous Effects of Invention

The colored glass plate of the present invention, despite the content of expensive cerium controlled to be low, simultaneously satisfies low solar transmittance, high visible light transmittance and low UV transmittance, while transmitted light has a green color tone.

DESCRIPTION OF EMBODIMENTS

The colored glass plate of the present invention is one containing SiO₂ as the main component, and it is preferably one made of so-called soda lime silica glass which further contains Na₂O, CaO, etc.

The colored glass plate of the present invention has the following composition (I). The colored glass plate of the present invention preferably has the following composition (II), more preferably has the following composition (III), further preferably has the following composition (IV).

(I) A composition comprising, as represented by mass percentage based on the following oxides,

-   -   SiO₂: from 65 to 75%,     -   Al₂O₃: from 0 to 6%,     -   MgO: from 0 to 6%,     -   CaO: from 5 to 15%,     -   total iron calculated as Fe₂O₃: from 0.3 to 1.2%,     -   total titanium calculated as TiO₂: from 0.2 to 1.1%,     -   total vanadium calculated as V₂O₅: from 0.02 to 0.3%, and     -   total cerium calculated as CeO₂: from 0.01 to 0.5%,         and containing substantially no cobalt, chromium or manganese.

(II) A composition comprising, as represented by mass percentage based on the following oxides,

-   -   SiO₂: from 65 to 75%,     -   Al₂O₃: from 0 to 6%,     -   MgO: from 0 to 6%,     -   CaO: from 5 to 15%,     -   Na₂O: from 5 to 18%,     -   total iron calculated as Fe₂O₃: from 0.3 to 1.2%,     -   total titanium calculated as TiO₂: from 0.2 to 1.1%,     -   total vanadium calculated as V₂O₅: from 0.02 to 0.3%, and     -   total cerium calculated as CeO₂: from 0.01 to 0.5%,         and containing substantially no cobalt, chromium or manganese.

(III) A composition comprising, as represented by mass percentage based on the following oxides,

-   -   SiO₂: from 68 to 73%,     -   Al₂O₃: from 0.5 to 3.5%,     -   MgO: from 2 to 6%,     -   CaO: from 6 to 11%,     -   Na₂O+K₂O: from 10 to 18%,     -   total iron calculated as Fe₂O₃: from 0.5 to 0.9%,     -   total titanium calculated as TiO₂: from 0.5 to 1.0%,     -   total vanadium calculated as V₂O₅: from 0.05 to 0.20%, and     -   total cerium calculated as CeO₂: from 0.05 to 0.30%,         and containing substantially no cobalt, chromium or manganese.

(IV) A composition comprising, as represented by mass percentage based on the following oxides,

-   -   SiO₂: from 70 to 72%,     -   Al₂O₃: from 1.5 to 2.0%,     -   MgO: from 2.5 to 5%,     -   CaO: from 7 to 9%,     -   Na₂O+K₂O: from 11 to 16%,     -   total iron calculated as Fe₂O₃: from 0.6 to 0.8%,     -   total titanium calculated as TiO₂: from 0.7 to 0.9%,     -   total vanadium calculated as V₂O₅: from 0.06 to 0.09%, and     -   total cerium calculated as CeO₂: from 0.08 to 0.20%,         and containing substantially no cobalt, chromium or manganese.

The colored glass plate of the present invention is characterized in that Tuv is maintained to be low by replacing a part of cerium by vanadium, Te is lowered by incorporating iron, and Tv is made high while making Dw to be from 540 to 570 nm as desired, by adjusting the content of total iron calculated as Fe₂O₃, the content of total titanium calculated as TiO₂, the content of total vanadium calculated as V₂O₅ and the content of total cerium calculated as CeO₂.

The content of total iron calculated as Fe₂O₃ is from 0.3 to 1.2%, as represented by mass percentage based on oxide. When the content of total iron calculated as Fe₂O₃ is at least 0.3%, it is possible to lower Te. As content of total iron calculated as Fe₂O₃ increases, Te lowers, but Tv also lowers. When the content of total iron calculated as Fe₂O₃ is made to be at most 1.2%, it is possible to prevent lowering of Tv and to bring Tv to be at least 70% (as calculated in a thickness of 4 mm). The content of total iron calculated as Fe₂O₃ is preferably from 0.5 to 0.9%, more preferably from 0.6 to 0.8%, as represented by mass percentage based on oxide.

The content of total titanium calculated as TiO₂ is from 0.2 to 1.1%, as represented by mass percentage based on oxide. When the content of TiO₂ is at least 0.2%, it is possible to adjust Dw to be at least 540 nm. Further, it is possible to lower Tuv. When the content of TiO₂ is at most 1.1%, it is possible to adjust Dw to be at most 570 nm. Further, it is possible to make Tv to be high. The content of total titanium calculated as TiO₂ is preferably from 0.5 to 1.0%, more preferably from 0.7 to 0.9%, as represented by mass percentage based on oxide.

The content of total vanadium calculated as V₂O₅ is from 0.02 to 0.3%, as represented by mass percentage based on oxide. When the content of V₂O₅ is at least 0.02%, it is possible to lower Tuv. When the content of V₂O₅ is at most 0.3%, it is possible to make Tv to be high. The content of total vanadium calculated as V₂O₅ is preferably from 0.05 to 0.20%, more preferably from 0.06 to 0.09%, as represented by mass percentage based on oxide.

The content of total cerium calculated as CeO₂ is from 0.01 to 0.5%, as represented by mass percentage based on oxide. When the content of CeO₂ is at least 0.01%, it is possible to lower Tuv. When the content of CeO₂ is at most 0.5%, it is possible to suppress the cost of the colored glass plate, and to make Tv to be high. The content of total cerium calculated as CeO₂ is preferably from 0.05 to 0.30%, more preferably from 0.08 to 0.20%, further preferably from 0.09 to 0.13%, as represented by mass percentage based on oxide.

The colored glass plate of the present invention contains substantially no cobalt, chromium or manganese which has, heretofore, been used as a typical colorant component. Here, “contains substantially no cobalt, chromium or manganese” means that cobalt, chromium or manganese is not contained at all, or cobalt, chromium or manganese may be contained as impurities unavoidably included during the production. When cobalt, chromium or manganese is not contained substantially, Tv can be made high, it is possible to prevent inclusion of impurities at the time of changing the base material, and the cost for the colored glass plate can be suppressed. The content of such impurities may vary depending upon the glass raw material to be used, but in the case of a glass plate for automobiles or buildings, it is preferably made to be less than 0.1%, more preferably less than 0.05%, further preferably less than 0.01%, as represented by mass percentage.

Here, “inclusion of impurities at the time of changing the base material” means the following.

During its production, glass may sometimes be switched to another glass type having a different glass composition (i.e. change of the base material). The inclusion of impurities at the time of changing the base material means that at the time of switching to another glass type, components of the glass before switching are included into the glass after switching. If inclusion of impurities such as cobalt, chromium, manganese, etc., takes place, after the switching, the color tone of the glass will be thereby substantially influenced.

SiO₂ is the main component of glass.

The content of SiO₂ is, as represented by mass percentage based on oxide, from 65 to 75%. When the content of SiO₂ is at least 65%, the weather resistance will be good. When the content of SiO₂ is at most 75%, devitrification is less likely to take place. The content of SiO₂ is, as represented by mass percentage based on oxide, preferably from 68 to 73%, more preferably from 70 to 72%.

Al₂O₃ is a component to improve the weather resistance.

The content of Al₂O₃ is, as represented by mass percentage based on oxide, from 0 to 6%. When the content of Al₂O₃ is at most 6%, the melting properties will be good. The content of Al₂O₃ is, as represented by mass percentage based on oxide, preferably from 0.5 to 3.5%, more preferably from 1.5 to 2.0%.

MgO is a component to accelerate melting of the glass raw material and to improve the weather resistance.

The content of MgO is, as represented by mass percentage based on oxide, from 0 to 6%. When the content of MgO is at most 6%, devitrification is less likely to take place.

The content of MgO is, as represented by mass percentage based on oxide, preferably from 2 to 6%, more preferably from 2.5 to 5%, further preferably from 3 to 4%, since the glass matrix composition raw material is thereby easily available, and it is possible to lower the cost of the colored glass plate.

On the other hand, a colored glass plate wherein the content of MgO is less than 2%, has lower Te, as compared with a colored glass plate wherein the content of MgO is at least 2%, at the same Tv. Therefore, when the content of MgO is less than 2%, it is possible to easily improve the heat ray absorption without impairing the visible light transmittance. The content of MgO is, as represented by mass percentage based on oxide, preferably at least 0% and less than 2%, more preferably from 0 to 1.0%, further preferably from 0 to 0.5%, with a view to sufficiently lowering Te while suppressing a decrease of Tv by the addition of a colorant component.

CaO is a component to accelerate melting of the glass raw material and to improve the weather resistance.

The content of CaO is, as represented by mass percentage based on oxide, from 5 to 15%. When the content of CaO is at least 5%, the melting properties and weather resistance will be good. When the content of CaO is at most 15%, devitrification is less likely to take place. The content of CaO is, as represented by mass percentage based on oxide, preferably from 6 to 11%, more preferably from 7 to 9%.

The colored glass plate of the present invention may contain SrO in order to accelerate melting of the glass raw material. The content of SrO is, as represented by mass percentage based on oxide, preferably from 0 to 5%, more preferably from 0 to 3%. When the content of SrO is at most 5%, the melting of the glass raw material can sufficiently be accelerated.

The colored glass plate of the present invention may contain BaO in order to accelerate melting of the glass raw material. The content of BaO is, as represented by mass percentage based on oxide, preferably from 0 to 5%, more preferably from 0 to 3%. When the content of BaO is at most 5%, the melting of the glass raw material can sufficiently be accelerated.

The colored glass plate of the present invention preferably contains Na₂O and K₂O, or Na₂O, in order to accelerate melting of the glass raw material. The total content of Na₂O and K₂O is, as represented by mass percentage based on oxides, preferably from 10 to 18%, more preferably from 11 to 16%, further preferably from 12 to 14%. When the content of Na₂O+K₂O is at least 10%, the melting properties will be good. When the content of Na₂O+K₂O is at most 18%, the weather resistance will be good.

The content of Na₂O is, as represented by mass percentage based on oxide, preferably from 5 to 18%, more preferably from 10 to 16%, further preferably from 12 to 15%.

The content of K₂O is, as represented by mass percentage based on oxide, preferably from 0 to 5%, more preferably from 0.2 to 1%, further preferably from 0.2 to 0.4%.

The colored glass plate of the present invention may contain SO₃ used as a fining agent. The content of SO₃ is, as represented by mass percentage based on oxide, preferably from 0 to 1%, more preferably from 0.01 to 0.5%, further preferably from 0.05 to 0.2%. When the content of SO₃ is at most 1%, the gas component of SO₂ is less likely to remain as gas bubbles in glass.

The colored glass plate of the present invention may contain SnO₂ used as a fining agent. The content of SnO₂ is, as represented by mass percentage based on oxide, preferably from 0 to 0.5%, more preferably from 0 to 0.3%, further preferably from 0 to 0.1%. When the content of SnO₂ is at most 0.5%, volatilization of SnO₂ tends to be less, and it is possible to suppress the cost to be low.

The specific gravity of the colored glass plate of the present invention is preferably from 2.49 to 2.55, more preferably from 2.50 to 2.52. By bringing the specific gravity of the colored glass plate of the present invention to be equal to usual soda lime silica glass, it is possible to improve the efficiency for changing the composition (i.e. changing the base material) at the time of the production.

The specific gravity of the colored glass plate of the present invention can be adjusted by adjusting the glass matrix composition. To adjust the specific gravity to the above level, the mass ratio of SiO₂/(MgO+CaO+SrO+BaO) is made to be preferably from 5.0 to 8.0, more preferably from 5.5 to 6.5. Here, (MgO+CaO+SrO+BaO) represents the total content of MgO, CaO, SrO and BaO which are contained.

Te (as calculated in a thickness of 4 mm) of the colored glass plate of the present invention is at most 55%, preferably at most 52%, more preferably at most 50%. Te is a solar transmittance calculated by measuring the transmittance by a spectrophotometer in accordance with JIS R3106 (1998) (hereinafter referred to simply as JIS R3106).

Tv (as calculated in a thickness of 4 mm) of the colored glass plate of the present invention is at least 70%, preferably at least 71.5%. Tv is a visible light transmittance calculated by measuring the transmittance by a spectrophotometer in accordance with JIS R3106. As the coefficient, a value of standard illuminant A, 2 degrees field of vision is employed.

Tuv (as calculated in a thickness of 4 mm) of the colored glass plate of the present invention is at most 12%, preferably at most 10%. Tuv is a UV transmittance calculated by measuring the transmittance by a spectrophotometer in accordance with ISO-9050.

The dominant wavelength (Dw) of transmitted light through the colored glass plate of the present invention is from 540 to 570 nm, preferably from 550 to 560 nm. When the dominant wavelength is within the above range, it is possible to obtain a colored glass plate whereby transmitted light has the desired green color tone. The dominant wavelength is one calculated by measuring the transmittance by a spectrophotometer in accordance with JIS Z8701 (1982). As the coefficient, a value of standard light C, 2 degrees field of vision is employed.

The colored glass plate of the present invention may be used for either vehicles or buildings and is particularly useful as a windshield or door glass for automobiles. In a case where it is to be used as a window glass for an automobile, as the case requires, it may be used in the form of laminated glass having a plurality of glass plates laminated with an interlayer, glass having flat glass processed to have a curved surface, or glass having tempering treatment applied. Otherwise, in a case where it is to be used as double-layered glass for buildings, it may be used in the form of double-layered glass composed of two colored glass plates of the present invention, or double-layered glass composed of a colored glass plate of the present invention and another glass plate.

The colored glass plate of the present invention may be produced, for example, via the following sequential steps (i) to (iv) and, as the case requires, further via a step (v).

(i) In order to attain a desired glass composition, glass matrix composition raw materials such as silica sand, etc., colorant component raw materials such as an iron source, a titanium source, a vanadium source, a cerium source, etc., an oxidizing agent, a reducing agent, a fining agent, etc., are suitably mixed to prepare a glass raw material.

(ii) The glass raw material is continuously supplied to a melting furnace, heated to from about 1,400 to 1,600° C. (e.g. about 1,500° C.) by heavy oil, etc. and melted to obtain molten glass.

(iii) The molten glass is refined and then formed into a glass plate having a prescribed thickness by e.g. a float process.

(iv) The glass plate is annealed and then cut into a prescribed size to obtain a colored glass plate of the present invention.

(v) As the case requires, the cut glass plate may be subjected to tempering treatment, may be processed into laminated glass, or may be processed into double-layered glass.

The glass matrix composition raw materials may be ones commonly used as raw materials for usual soda lime silica glass, such as silica sand, an alumina source, a magnesia source, a calcia source, an alkali oxide source, etc.

The iron source may, for example, be iron powder, iron oxide powder, rouge, etc.

The titanium source may, for example, be titanium oxide, etc.

The vanadium source may, for example, be vanadium oxide, etc.

The oxidizing agent may, for example, be sodium nitrate, etc. The oxidizing agent is one to accelerate oxidation of iron in molten glass.

The cerium source may, for example, be cerium oxide, etc.

The reducing agent may, for example, be carbon, coke, etc. The reducing agent is one to prevent oxidation of iron in molten glass.

Further, SnO₂ may be used as a reducing agent or a fining agent, and SO₃ may be used as an oxidizing agent or a fining agent.

In the colored glass plate of the present invention as described above, as represented by mass percentage based on oxide, total iron calculated as Fe₂O₃ is from 0.3 to 1.2%, total titanium calculated as TiO₂ is from 0.2 to 1.1%, total vanadium calculated as V₂O₅ is from 0.02 to 0.3%, and total cerium calculated as CeO₂ is from 0.01 to 0.5%, whereby despite the content of expensive cerium controlled to be low and containing substantially no other colorant components (such as cobalt, etc.), it satisfies Te≦55% (as calculated in a thickness of 4 mm), Tv≧70% (as calculated in a thickness of 4 mm) and Tuv≦12% (as calculated in a thickness of 4 mm), while transmitted light has a green color tone.

EXAMPLES

Now, the present invention will be described specifically with reference to Examples, but it should be understood that the present invention is by no means limited to such Examples.

Ex. 1 to 3 are Examples of the present invention, and Ex. 4 is a Comparative Example.

(Te)

With respect to an obtained glass plate, the solar transmittance (Te) as stipulated in JIS R3106 was obtained as a value calculated in a thickness of 4 mm.

(Tv)

With respect to an obtained glass plate, the visible light transmittance (Tv) (illuminant A, 2 degrees field of vision) as stipulated in JIS R3106 was obtained as a value calculated in a thickness of 4 mm.

(Tuv)

With respect to an obtained glass plate, the UV transmittance (Tuv) as stipulated in ISO-9050 was obtained as a value calculated in a thickness of 4 mm.

(Dw)

With respect to an obtained glass plate, the dominant wavelength (Dw) of transmitted light as stipulated in JIS Z8701 (1982) was obtained.

Ex. 1 to 4

The respective raw materials were mixed to attain the composition shown in Table 1, and further, Na₂SO₄ was mixed as an oxidizing agent in the amount shown in Table 1 as calculated as SO₃, to prepare a glass raw material. The glass raw material was put in a crucible and heated to 1,500° C. in an electric furnace to obtain molten glass. The molten glass was cast on a carbon plate and cooled. Both sides were polished to obtain a glass plate having a thickness of 4 mm. With respect to the obtained glass plate, the transmittances were measured for every 1 nm by means of a spectrophotometer (Lambda 950, manufactured by Perkin Elmer) to obtain Te, Tv, Tuv and Dw. The results are shown in Table 1.

TABLE 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Composition (%) SiO₂ 71.4 71.5 71.3 70.8 Al₂O₃ 1.9 1.9 1.9 1.5 MgO 3.7 3.7 3.7 3.9 CaO 8.0 8.0 8.0 8.1 Na₂O 12.9 13.0 12.9 13.8 K₂O 0.3 0.3 0.3 0.3 Fe₂O₃ 0.70 0.70 0.70 0.81 TiO₂ 0.81 0.61 0.81 0.42 V₂O₅ 0.07 0.07 0.08 0 CeO₂ 0.10 0.10 0.10 0.09 CoO 0 0 0 0 Cr₂O₃ 0 0 0 0 MnO 0 0 0 0 Oxidizing agent (%) SO₃ 0.1 0.1 0.2 0.3 Tv (%/4 mmt) 72.5 72.7 72.4 73.2 Te (%/4 mmt) 49.0 48.6 49.0 45.8 Tuv (%/4 mmt) 9.9 10.9 9.5 14.9 Dw (nm) 556 551 556 533

The colored glass plate of the present invention in each of Ex. 1 to 3 satisfied Te≦55% (as calculated in a thickness of 4 mm), Tv≧70% (as calculated in a thickness of 4 mm) and Tuv≦12% (as calculated in a thickness of 4 mm), while transmitted light had a green color tone with its dominant wavelength being within a range of from 540 to 570 nm.

The colored glass plate in Ex. 4 contained no V₂O₅, whereby Tuv was high.

INDUSTRIAL APPLICABILITY

The colored glass plate of the present invention is useful as a glass plate for vehicles and buildings, and is particularly suitable as a glass plate for automobiles.

This application is a continuation of PCT Application No. PCT/JP2013/051659, filed on Jan. 25, 2013, which is based upon and claims the benefit of priority from Japanese Patent Application No. 2012-015562 filed on Jan. 27, 2012. The contents of those applications are incorporated herein by reference in their entireties. 

What is claimed is:
 1. A colored glass plate comprising, as represented by mass percentage based on oxides: SiO₂: from 65 to 75%, Al₂O₃: from 0 to 6%, MgO: from 0 to 6%, CaO: from 5 to 15%, total iron calculated as Fe₂O₃: from 0.5 to 1.2%, total titanium calculated as TiO₂: from 0.2 to 1.1%, total vanadium calculated as V₂O₅: from 0.02 to 0.3%, and total cerium calculated as CeO₂: from 0.01 to 0.5%, wherein said colored glass plate comprises substantially no cobalt, chromium or manganese and has: a solar transmittance as stipulated in JIS R3106 (1998) of at most 55% as a value calculated in a thickness of 4 mm, a visible light transmittance (illuminant A, 2 degrees field of vision) as stipulated in JIS R3106 (1998) of at least 70% as a value calculated in a thickness of 4 mm, an UV transmittance as stipulated in ISO-9050 of at most 12% as a value calculated in a thickness of 4 mm, and a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 540 to 570 nm.
 2. The colored glass plate according to claim 1, which further comprises, as represented by mass percentage based on oxides, from 5 to 18% of Na₂O.
 3. The colored glass plate according to claim 1, which has a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 551 to 556 nm.
 4. The colored glass plate according to claim 1, comprising, as represented by mass percentage based on oxides: SiO₂: from 68 to 73%, Al₂O₃: from 0.5 to 3.5%, MgO: from 2 to 6%, CaO: from 6 to 11%, Na₂O+K₂O: from 10 to 18%, total iron calculated as Fe₂O₃: from 0.5 to 0.9%, total titanium calculated as TiO₂: from 0.5 to 1.0%, total vanadium calculated as V₂O₅: from 0.05 to 0.20%, and total cerium calculated as CeO₂: from 0.05 to 0.30%.
 5. The colored glass plate according to claim 1, comprising, as represented by mass percentage based on oxides: SiO₂: from 70 to 72%, Al₂O₃: from 1.5 to 2.0%, MgO: from 2.5 to 5%, CaO: from 7 to 9%, Na₂O+K₂O: from 11 to 16%, total iron calculated as Fe₂O₃: from 0.6 to 0.8%, total titanium calculated as TiO₂: from 0.7 to 0.9%, total vanadium calculated as V₂O₅: from 0.06 to 0.09%, and total cerium calculated as CeO₂: from 0.08 to 0.20%.
 6. The colored glass plate according to claim 1, wherein the content of cobalt, chromium and manganese in the colored glass plate is less than 0.05% as represented by mass percentage.
 7. The method according to claim 1, wherein the content of cobalt, chromium and manganese in the colored glass plate is less than 0.01% as represented by mass percentage.
 8. The method according to claim 1, wherein the colored glass plate comprises no cobalt, chromium or manganese.
 9. The colored glass plate according to claim 1, which has a solar transmittance as stipulated in JIS R3106 (1998) of at most 50% as a value calculated in a thickness of 4 mm, a visible light transmittance (illuminant A, 2 degrees field of vision) as stipulated in JIS R3106 (1998) of at least 71.5% as a value calculated in a thickness of 4 mm, an UV transmittance as stipulated in ISO-9050 of at most 10% as a value calculated in a thickness of 4 mm, and a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 550 to 560 nm.
 10. The colored glass plate according to claim 9, comprising, as represented by mass percentage based on oxides: SiO₂: from 68 to 73%, Al₂O₃: from 0.5 to 3.5%, MgO: from 2 to 6%, CaO: from 6 to 11%, Na₂O+K₂O: from 10 to 18%, total iron calculated as Fe₂O₃: from 0.5 to 0.9%, total titanium calculated as TiO₂: from 0.5 to 1.0%, total vanadium calculated as V₂O₅: from 0.05 to 0.20%, and total cerium calculated as CeO₂: from 0.05 to 0.30%.
 11. The colored glass plate according to claim 10, which has a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 551 to 556 nm.
 12. The colored glass plate according to claim 9, comprising, as represented by mass percentage based on oxides: SiO₂: from 70 to 72%, Al₂O₃: from 1.5 to 2.0%, MgO: from 2.5 to 5%, CaO: from 7 to 9%, Na₂O+K₂O: from 11 to 16%, total iron calculated as Fe₂O₃: from 0.6 to 0.8%, total titanium calculated as TiO₂: from 0.7 to 0.9%, total vanadium calculated as V₂O₅: from 0.06 to 0.09%, and total cerium calculated as CeO₂: from 0.08 to 0.20%.
 13. The colored glass plate according to claim 12, which has a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 551 to 556 nm.
 14. The colored glass plate according to claim 13, wherein the content of cobalt, chromium and manganese in the colored glass plate is less than 0.05% as represented by mass percentage.
 15. The method according to claim 13, wherein the content of cobalt, chromium and manganese in the colored glass plate is less than 0.01% as represented by mass percentage.
 16. The method according to claim 13, wherein the colored glass plate comprises no cobalt, chromium or manganese.
 17. A method for producing the colored glass plate according to claim 1, which comprises melting glass raw materials, followed by forming to obtain said colored glass.
 18. The method for producing a colored glass plate according to claim 17, wherein the glass plate further comprises, as a compositional component and as represented by mass percentage based on oxide, from 5 to 18% of Na₂O.
 19. The method for producing a colored glass plate according to claim 17, wherein the colored glass plate produced has: a solar transmittance as stipulated in JIS R3106 (1998) of at most 50% as a value calculated in a thickness of 4 mm, a visible light transmittance (illuminant A, 2 degrees field of vision) as stipulated in JIS R3106 (1998) of at least 71.5% as a value calculated in a thickness of 4 mm, an UV transmittance as stipulated in ISO-9050 of at most 10% as a value calculated in a thickness of 4 mm, and a dominant wavelength of transmitted light as stipulated in JIS Z8701 (1982) of from 550 to 560 nm. 